Epoxy resins, hardeners and gelcoats

Showing 49-72 of 101 item(s)

-Kč97.83

Hardener 500 MGS

001024

Hardener for epoxy resin 285 with a mixing ratio of 100:40 by weight and 100:50 by volume. Processing time is 10-15 min at 20°C. Suitable for fast curing at low temperatures from +10°C.

Kč1,043.50 Kč1,141.33

Time left

-Kč127.47

Hardener F 250 /MGS/

001057

Hardener F 200 for molding resin with a mixing ratio of 100:25. Processing time is 15-20 min at 25°C, with a gel time of 1-2 h and curing time of 24 h. Suitable for molds without heat resistance.

Kč764.84 Kč892.31

Time left

Havel Adhesive G 40 (A5 + B30) is an epoxy adhesive system suitable for bonding laminate parts at 10 - 30°C. For optimal curing, temper for 4.5 hours at 45 - 60°C. Recommended hardener B 30 in a 100:17 weight ratio. Working time: 30-40 minutes.

Kč1,019.89

Havel Adhesive G 40 sl.A 5

eshop_111120

Structural adhesive for bonding laminate and wooden parts, suitable for polyester resin. Ideal for imprecise parts needing gap filling. High viscosity, processing time 20-40 minutes. Mix ratios: B 20 (100:13 +/- 2g), B 30 (100:17 +/- 2g). Curing can be accelerated at 40-60°C.

Kč1,182.26

HAVELcell E1 složka A

eshop_111101

HAVELcell E1 is a lightweight epoxy foam (550 kg/m3) ideal for sandwich constructions and boat manufacturing. Coated with fiberglass, it is lighter than water. Use with HAVELcell E1 hardener (100:35 ratio) and has a processing time of 30 minutes.

Kč860.16

HAVELcell E1 složka B

eshop_111102

HAVELcell E1 component B is a hardener for curing epoxy foam HAVELcell E1 component A at a 100:35 weight ratio.

Kč1,169.82

LH 260 s odpěnovačem

eshop_112218/1

Epoxy resin LH 260 with silicone-free defoamer, low viscosity, high mechanical properties, good chemical resistance, and excellent thermal properties. Suitable for laminating with glass, carbon, and Kevlar fibers. Can be pigmented. Key properties: liquid state, weight equivalent 176-184 g/mol, max Gardner color 3, epoxy index 0.53-0.58, flash point...

Kč531.47

Ředidlo pro epoxidový stříkací gelcoat EG 100-W a EG 100-T

eshop_001047

Thinner for epoxy solvent-based coatings, altering gelcoat viscosity for spray application. Use 5-20% for optimal results.

Kč500.72

Tužidlo 133 (MGS)

eshop_001017

Hardener for epoxy resin with a mixing ratio of 100:35 (weight) or 100:40 (volume). Working time is 10-15 minutes at 20°C. Minimum order is 25kg.

Kč933.36

Tužidlo 134 (MGS)

eshop_001018

Hardener for epoxy resin L 135, L 160, L, LR, LR 100, LH 160. Mixing ratio: 100:35 (weight) or 100:40 (volume). Processing time for 100g at 20°C is 20 min. Refer to technical data sheets MGS for detailed instructions.

Kč819.90

View

Tužidlo 135 (MGS)

eshop_001008/1

Hardener for epoxy resin L 135, L 160, L, LR, LR 100, LH 160. Mixing ratio: 100:35 (weight) or 100:40 (volume). Working time: 25-30 min for 100g at 20°C. More info at http://www.momentive.com/

Kč819.90

Tužidlo 136 (MGS)

eshop_001019

Hardener for epoxy resin L 135, L 160, L, LR, LR 100, LH 160. Mixing ratio: 100:35 (weight) or 100:40 (volume). Working time for 100g at 20°C: 1 - 2 hours. More info at http://www.momentive.com/

Kč948.74

Tužidlo 285 (MGS)

eshop_001009

Hardener for epoxy resin 285 with a mixing ratio of 100:40 (weight) / 100:50 (volume). Processing time is 50 minutes for 100g at 20°C. Available in 25 and 200 kg packaging. More info at http://www.momentive.com/

Kč1,172.74

Tužidlo 286 (MGS)

eshop_001010

Hardener for epoxy resin 285 with a mixing ratio of 100:40 (weight) / 100:50 (volume). Processing time is 2 hours at 20°C for 100g. Available in 25 kg and 200 kg packaging. More info at http://www.momentive.com/

Kč1,156.27

Tužidlo 287 (MGS)

eshop_001011

Hardener for epoxy resin 285 with a mixing ratio of 100:40 (weight) / 100:50 (volume). Processing time is 4 hours at 20°C for 100g. Available in 25 kg and 200 kg packaging. More info at http://www.momentive.com/

Kč1,583.95

Tužidlo 7067 do gelcoatu

eshop_900883

Hardener for transparent gelcoat 7060.

Kč1,434.82

Tužidlo C

eshop_001030

Hardener for epoxy resin C with a mixing ratio of 100:60 (by weight) and a processing time of 50 minutes. See R+G Handbook p. 77/78 for details.

Kč812.58

Tužidlo H 10

eshop_111070

Hardener H 10 is designed for curing epoxy systems with enhanced UV stability for applications like casting, laminating, and coatings. It works at temperatures as low as 10°C and offers excellent smoothness. Suitable for laminates with glass fabrics, with a mixing ratio of 100:45-50. Not recommended for clear castings or jewelry.

Kč566.61

Tužidlo H 100 do epoxidového stříkacího gelcoatu EG 100-W a EG 100-T

eshop_001046

Hardener for epoxy gelcoats, mixed in specific ratios for EG 100 T and EG 100 W. Ensure thorough mixing and avoid exposure to weather or chemicals until fully cured.

Kč1,200.56

Tužidlo H 10A

eshop_111224

Hardener H 10A is a liquid modified adduct hardener suitable for clear laminating systems, particularly for visible layers. It has a processing time of 30-40 minutes and is compatible with various epoxy resins. The cured composite is not brittle, with a gel time of 3-5 hours in a 1mm thick layer.

Kč659.58

Tužidlo H 10B

eshop_111227

Hardener combined with LH 160 and LH 210 in a 100:47 ratio, ideal for self-adhesive labels. Achieves a bubble-free surface in 1-2mm layers and becomes non-sticky after 16-24 hours, resulting in a clear, flexible composite.

Kč581.98

Tužidlo H 145 (HAVEL)

eshop_111032

Mixing ratio 100:33, working time 50 min. Requires tempering to at least 50°C.

Kč579.78

Tužidlo H 146

eshop_111198

High-quality hardener for epoxy resins with a mixing ratio of 100:30 (LH 160, LH 145, LH 130). Working time: 50-60 min. Minimum curing temperature: 25 °C (recommended: 30 °C+).

Kč512.44

Tužidlo H 147 (HAVEL)

eshop_111030

High-performance epoxy hardener LH 160 for certified parts, mixing ratio 100:25, 90 min working time, requires curing at 50°C. Achieves thermal resistance of 100°C with gradual curing up to 85°C for 8 hours. High quality with fewer harmful emissions.