Tužidlo H 10A

Hardener H 10A is a hardener as a replacement for H10. This hardener is particularly suitable for applications where a clear laminating system is required. For example, for visible layers made from fiberglass with an aluminum surface or in cases where the clearest laminate possible needs to be produced. Hardener H 10A is a liquid modified adduct hardener containing cycloaliphatic amine for low molecular weight epoxy resins. Hardener H 10A is characterized by a shorter processing time of 30-40 minutes. Hardener H 10A is a hardener as a replacement for H10 for epoxy resins. It is suitable for all types of laminations at temperatures above 15°C. Processing time is 30 – 40 minutes. Ratio to resin LH 160 : H 10 A = 100 : 50. Ratio to resin LH 260 : H 10A = 100 : 50. Ratio to resin LH 289 : H 10 A = 100 : 50. Ratio to resin LH 288 : H 10 A = 100 : 50. The cured composite is not brittle. Gel time in a 1mm thick layer is 3-5 hours.